Cast Duplex Stainless Steel CD4MCuN |
|
|
CD4MCuN is CD4MCu modified with nitrogen to improve corrosion resistance, strength, weldability, and castability. It is resistant to some concentrations of sulfuric and dilute hydrochloric acids; acid and wet process phosphoric acid slurries; stress corrosion cracking in chloride containing solutions and fumes; concentrated brine and seawater; fatty acids; pulp liquors at 220°F (104°C); and steam. CD4MCuN is able to handle soft abrasives and is used in some corrosion-erosion service applications. It is used in a variety of industries including chemical processing, marine, municipal water supply, naval, paint, petroleum refining, power plant, pulp and paper, soap manufacturing, textile, and transportation. Applications include processing equipment requiring higher strength than CF8, compressor cylinders, digester valves, feed screws, pump impellers, liners, pump casings, runway light fixtures, and centrifugal pumps seal ring
|
|
|
ASTM A890 A995 UNS S39205 |
Equivalent Grades |
|
1450 |
Melting Point(oC) |
|
Heat to 1120°C minimum, hold for sufficient time to heat casting uniformly to temperature and water quench, or the casting may be furnace cooled to 1010°C minimum, hold for 15 min minimum and then water quench. A rapid cool by other means may be employed in lieu of water quench. |
Heat Treatment |
|
250 |
Hardness (HB) |
|
E2209-15 |
Welding Electrode |
|
- |
Welding Preheating(oC) |
|
Gas Porosity, chemical composition due to Carbon content |
Common Possible Casting Defects |